Coordination-Bond-Driven Dissolution-Recrystallization Structural Transformation with the Expansion of Cuprous Halide...

Metal-organic frameworks (MOFs) with cuprous-halide-aggregates have shown superiority as organic LED (OLED) and semiconductor materials, while engineering MOF flexibility by involving the expansion of cuprous aggregates remains a great challenge. In this particular work, a dissolution-recrystallization structural transformation (DRST) with the dramatic growth of Cu^I-I aggregates, from 2D NJNU-100 to 3D NJNU-101 has been successfully realized. The unsaturated coordination nodes (2-positional nitrogen atoms) in NJNU-100 have been demonstrated to be the driven force for DRST to NJNU-101 via the formation of coordination bonds. The structural transformation process was irreversible and observed with optical microscopy and powder XRD. The expansion of Cu^I-I aggregates was also computational simulated accompanying with the rotation of the neutral tripodal TTTMB ligand (1,3,5-tris(1,2,4-triazol-1-ylmethyl)-2,4,6-trimethylbenzene) and the reduction of Cu^II to Cu^I. Moreover, the intermediate product NJNU-102 was captured by adding the planar molecular anthrancene to shut down the reaction, where only partial 2-positional nitrogen atoms coordinated to the aggregates and the anthrancene was oxidized to anthraquinone. NJNU-102 has further confirmed that DRST involved the breakage and recombination of coordination bonds and the electron transfer. NJNU-100 and NJNU-101 could be applied as semiconductor and OLED materials. This work has provided insights for crystal engineering, especially for the construction of the Cu^IX aggregates, and illustrated that DRST could be controlled with a rational design (as the unsaturated coordination modes).