Dilatometric and Microstructural Study of Martensite Tempering in 4% Mn Steel

Adam Grajcar1, Mateusz Morawiec1, Jose Antonio Jimenez2

  • 1Department of Engineering Materials and Biomaterials, Silesian University of Technology, 44-100 Gliwice, Poland.

Materials (Basel, Switzerland)
|October 10, 2020
PubMed

Keywords:
cementite precipitationdilatometrymartensitic transformationmedium-Mn steelquenchingtempering

More Related Videos

An Available Technique for Preparation of New Cast MnCuNiFeZnAl Alloy with Superior Damping Capacity and High Service Temperature14:51

An Available Technique for Preparation of New Cast MnCuNiFeZnAl Alloy with Superior Damping Capacity and High Service Temperature

Published on: September 23, 2018

7.3K
Micromechanical Tension Testing of Additively Manufactured 17-4 PH Stainless Steel Specimens05:38

Micromechanical Tension Testing of Additively Manufactured 17-4 PH Stainless Steel Specimens

Published on: April 7, 2021

3.7K

Related Concept Videos

Mechanical Characteristics of Steel01:18

Mechanical Characteristics of Steel

The mechanical characteristics of steel are assessed through various tests that evaluate its strength, toughness, and flexibility. These tests include tension, torsion, impact, bending, and hardness assessments, each providing crucial information about steel's suitability for specific applications.
The tension test is fundamental for determining tensile strength. In this test, a steel specimen is stretched using a gripping device until it breaks. The data collected during this test are used...
911
Temperature Dependent Deformation01:12

Temperature Dependent Deformation

In a nonhomogeneous rod made up of steel and brass, restrained at both ends and subjected to a temperature change, several steps are involved in calculating the stress and compressive load. Due to the problem's static indeterminacy, one end support is disconnected, allowing the rod to experience the temperature change freely. Next, an unknown force is applied at the free end, triggering deformations in the rod's steel and brass portions. These deformations are then calculated and added...
296
Ferromagnetism01:31

Ferromagnetism

Materials like iron, nickel, and cobalt consist of magnetic domains, within which the magnetic dipoles are arranged parallel to each other. The magnetic dipoles are rigidly aligned in the same direction within a domain by quantum mechanical coupling among the atoms. This coupling is so strong that even thermal agitation at room temperature cannot break it. The result is that each domain has a net dipole moment. However, some materials have weaker coupling, and are ferromagnetic at lower...
2.8K
Stress-Strain Diagram - Ductile Materials01:24

Stress-Strain Diagram - Ductile Materials

The stress-strain relationship in ductile materials such as structural steel or aluminium is intricate and progresses through several stages. When a specimen is loaded, it initially exhibits a linear length increase, depicted by a steep straight line on the stress-strain diagram. It indicates the material is elastically deforming and will return to its original shape once unloaded. However, when a critical stress value is reached, plastic deformation begins. This stage sees substantial...
1.6K
Microcracking in Concrete01:20

Microcracking in Concrete

Microcracking in concrete refers to the tiny cracks that can form within the material even before any external load is applied. These microcracks typically occur at the interface between the coarse aggregate and the hydrated cement paste, often as a result of differential volume changes prompted by variations in stress-strain behavior, as well as thermal and moisture movement. Initially, these microcracks remain stable and do not grow substantially until the concrete is stressed to about 30...
319