Experimental Investigation and FEM Simulation of the Tensile Behavior of Hot-Rolled Quenching and Partitioning 5Mn...

Medium manganese steels provide a good combination of tensile strength and ductility due to their multiphase microstructure produced during the multi-step heat treatment process. This study primarily focused on testing and analyzing the tensile properties of 0.17C-5Mn-0.76Al-0.9Si-Nb medium manganese quenching and partitioning (QP) steel using both the experimental and finite element method (FEM) in the multilinear isotropic hardening material model. The 7 mm and 12 mm thick plates exhibited a similar microstructure of tempered primary martensite, lath-type retained austenite, and secondary martensite. The experiments measured tensile strengths of 1400 MPa for 12 mm round specimens and 1325 MPa for 7 mm flat specimens, with total elongations of 15% for round specimens and 11% for flat specimens. The results indicated that the sample's geometry has some effect on the UTS and ductility of the studied medium-Mn QP steel. However, the more important is the complex relationship between the plate thickness and yield stress and ductility, which are affected by finishing hot rolling conditions. The FEM results showed that the von Mises stresses for flat and round specimens were 1496 MPa and 1514 MPa, respectively, and were consistent with the calculated true stresses of experimental results. This shows that numerical modeling, specifically a multilinear isotropic hardening material model, properly describes the material properties beyond the yield stress and accurately predicts the plastic deformation of the investigated multiphase QP steel.