Apical Sealing Ability of Calcite-Synthesized Hydroxyapatite as a Filler of Epoxy Resin-Based Root Canal Sealer

The success of root canal treatment is influenced by hermetic root canal obturation. This study was conducted to analyze the apical sealing ability after the addition of calcite-synthesized hydroxyapatite (HA) as an epoxy resin sealer filler.

Calcite-synthesized HA powder was prepared using the microwave hydrothermal process. HA resin sealer powder and epoxy resin paste (3:1) were mixed, and concentrations of 10%, 20%, 30%, 40%, and 50% were prepared. A sample of thirty maxillary incisors were prepared in the root canal and then, the crown was cut to leave 13 mm of the root and a working length of 12 mm. The root canal was prepared using the crown-down technique and irrigated using 2.5% sodium hypochlorite and 17% ethylenediaminetetraacetic acid alternately. The samples were divided into six groups, with each group consisting of five roots. Group I was obturated with gutta percha using an epoxy resin sealer without HA (HA-0%) as a control group. In each of the Groups II, III, IV, V, and VI, 10% HA resin sealer, 20% HA, 30% HA, 40% HA, and 50% HA were used. All the samples were incubated in a 10-ml simulated body fluid solution at 37°C for 4 weeks. Apical closure density measurement was done using a scanning electron microscope, and the results were analyzed using the Kruskal-Wallis and Mann-Whitney U-tests.

A significant increase in the apical sealing ability was observed in the HA-20% sealer group and the HA-30% and HA-40% groups compared to that in the control group. However, the HA-50% sealer group showed a decrease in the apical sealing ability, whereas the HA-10% sealer group showed no difference. The HA-30% had the highest sealing ability than other concentrations.

The addition of calcite-synthesized HA as a filler at concentrations of 20%, 30%, and 40% increased the apical sealing ability of the epoxy resin sealer.