Influence of abutment angulation on loss of prosthetic abutment torque under mechanical cycling

Internal conical connections provide mechanical stability for the prosthetic abutment and implant connection. However, some clinical situations require the use of angled prosthetic abutments that may increase stress on supportive implants by difference force vectors under cyclic loading.

The purpose of this in vitro study was to measure the screw loosening values of prosthetic abutments with internal conical connections (indexed and nonindexed) having different angles under mechanical cycling.

Thirty-six implants (4.0×13 mm, Titamax) with internal conical connections and their respective universal prosthetic abutments (n=36, 3.5×3.3 mm) were divided into indexed and nonindexed groups (n=18) with abutment inclinations of 0 (straight), 17, and 30 degrees. An insertion torque of 15 Ncm was applied according to the manufacturer's specifications. The specimens underwent fatigue testing of 500 000 cycles at a frequency of 2 Hz with a dynamic compressive load of 120 N at an angle of 30 degrees. The detorque values were measured by using a digital torque meter and tabulated for statistical analyses.

The specimens with indexed abutments had mean ±standard deviation detorque values of 6.72 ±2.29 Ncm under mechanical cycling, whereas those with nonindexed abutments had values of 8.98 ±1.84 Ncm. In the indexed group, the lowest detorque value was observed for abutments at 30 degrees compared with the straight group (P<.05). As for nonindexed abutments, similar detorque values were observed after increasing the abutment inclination (P>.05).

A decrease in detorque values in the indexed abutments related to their inclination was found under mechanical cycling, whereas the prosthetic abutments with 30 degrees of angulation had the lowest values. No decrease was found in the nonindexed abutments.