The Correlation of Temperature-Mineral Phase Transformation as a Controlling Factor of Thermal and Mechanical...

This research focuses on an evaluation of mineral phase and structure transformations in Class F fly ash-based geopolymer systems. The research also studies the strength response of geopolymers when exposed to temperatures between 25 and 800 °C. The purpose of this research is to understand the processes that occur in alkali-activated systems within a wide range of high-working temperatures. The XRD, SEM, and DTA/TG analyses performed for the alkali-activated compositions after exposure to different temperatures confirmed a direct correlation of structural transformations with strength performance. The detrimental effect of sodium hydrocarbonate Na₃(HCO₃)(CO₃) 2H₂O or trona contained in one of the fly ash products was observed for the corresponding alkali-activated composite under high-temperature exposure between 600 and 800 °C. It was also detected that a high-temperature interval of 400-800 °C created favorable conditions that helped to form nanosized nepheline crystals and an additional vitreous substance that also contributed to a denser alkali-activated matrix.