Ultrafast and Long-Lived Transient Heating of Surface Adsorbates on Plasmonic Semiconductor Nanocrystals

Plasmonic photocatalysts have demonstrated promising potential for enhancing the selectivity and efficiency of important chemical transformations. However, the relative contributions of nonphotothermal (i.e., hot carrier) and photothermal pathways remain a question of intense current debate, and the time scale and extent of surface adsorbate temperature change are still poorly understood. Using p-type Cu_2-Se nanocrystals as a semiconductor plasmonic platform and adsorbed Rhodamine B as a surface thermometer and hot carrier acceptor, we measure directly by transient absorption spectroscopy that the adsorbate temperature rises and decays with time constants of 1.4 ± 0.4 and 471 ± 126 ps, respectively, after the excitation of Cu_2-Se plasmon band at 800 nm. These time constants are similar to those for Cu_2-Se lattice temperature, suggesting that fast thermal equilibrium between the adsorbates and nanocrystal lattice is the main adsorbate heating pathway. This finding provides insights into the transient heating effect on surface adsorbates and their roles in plasmonic photocatalysis.