A Novel Silicon/Phosphorus Co-Flame Retardant Polymer Electrolyte for High-Safety All-Solid-State Lithium Ion...

Developing a solid polymer electrolyte with superior flame retardancy and lithium-ion transportation properties is still a challenge. Herein, an intrinsic silicon/phosphorus co-flame retardant polymer solid electrolyte was prepared by using polyethylene glycol (PEG) co-polymerized with silicon and phosphorus-containing monomers. Due to the synergistic flame-retardant effect of silicon and phosphorus elements, this polymer electrolyte exhibits excellent thermal stability and flame resistance. Moreover, the ionic conductivity of the electrolyte at 25 °C is as high as 2.98 × 10^-5 S/cm when the mass ratio of LiN(SO₂CF₃)₂ (LiTFSI) and the prepared polymer electrolyte is 10:1. What is more, the LiFePO₄/Li all-solid-state battery assembled with this solid electrolyte can work stably at a high temperature of 60 °C and exhibits a specific capacity of 129.2 mAh/g at 0.2 C after 100 cycles, providing a promising application prospect for high-safety lithium-ion batteries.