Effect of Titanium and Boron Microalloying on Sulfide Stress Cracking in C110 Casing Steel

Ming Luo1,2, Zhong-Hua Zhang2, Yao-Heng Liu2

  • 1Institute of Materials, School of Materials Science and Engineering, Shanghai University, 149 Yanchang Road, Shanghai 200072, China.

Materials (Basel, Switzerland)
|December 18, 2020
PubMed

Keywords:
Ti and Bcasing steelhardenabilityprior austenite grain sizesulfide stress cracking

More Related Videos

Full-field Strain Measurements for Microstructurally Small Fatigue Crack Propagation Using Digital Image Correlation Method07:37

Full-field Strain Measurements for Microstructurally Small Fatigue Crack Propagation Using Digital Image Correlation Method

Published on: January 16, 2019

10.0K
Spark Plasma Sintering Apparatus Used for the Formation of Strontium Titanate Bicrystals11:17

Spark Plasma Sintering Apparatus Used for the Formation of Strontium Titanate Bicrystals

Published on: February 9, 2017

10.1K

Related Concept Videos

Microcracking in Concrete01:20

Microcracking in Concrete

Microcracking in concrete refers to the tiny cracks that can form within the material even before any external load is applied. These microcracks typically occur at the interface between the coarse aggregate and the hydrated cement paste, often as a result of differential volume changes prompted by variations in stress-strain behavior, as well as thermal and moisture movement. Initially, these microcracks remain stable and do not grow substantially until the concrete is stressed to about 30...
290
Mechanical Characteristics of Steel01:18

Mechanical Characteristics of Steel

The mechanical characteristics of steel are assessed through various tests that evaluate its strength, toughness, and flexibility. These tests include tension, torsion, impact, bending, and hardness assessments, each providing crucial information about steel's suitability for specific applications.
The tension test is fundamental for determining tensile strength. In this test, a steel specimen is stretched using a gripping device until it breaks. The data collected during this test are used...
889
Yield Criteria for Ductile Materials under Plane Stress01:25

Yield Criteria for Ductile Materials under Plane Stress

In designing structural elements and machine parts using ductile materials, it is crucial to ensure that these components withstand applied stresses without yielding. Yielding is initially determined through a tensile test, which evaluates the material's response to uniaxial stress. However, tensile stress is insufficient when components face biaxial or plane stress conditions This condition requires advanced criteria to predict failure.
The Maximum Shearing Stress Criterion, also known as...
317
Fatigue01:21

Fatigue

Fatigue occurs when materials rupture under repeated or fluctuating loads, even at stress levels far below their static breaking strength. It typically results in brittle failure, even for ductile materials. It is a critical consideration in designing machines and structural components subjected to repetitive or varying loads. The nature of these loadings can range from fluctuating loads like unbalanced pump impellers causing vibrations to repeatedly bending a thin steel rod wire back and forth...
517
Bearing Stress01:22

Bearing Stress

Bearing stress refers to the contact pressure between two separate bodies. To visualize this, imagine a bolt thrust through a plate. The bolt applies a force to the plate, which exerts an equal but opposite force back onto the bolt. This force isn't just a singular entity but a compilation of numerous smaller forces distributed across the contact surface between the bolt and the plate.
Due to the intricacy of these microforces, an average value, known as bearing stress, is often used by...
1.5K
Torsion of Noncircular Members01:16

Torsion of Noncircular Members

Circular shafts undergoing torsional stress maintain their cross-sectional integrity due to their axisymmetric nature. This symmetry ensures an even distribution of stress, allowing the shaft to withstand torsion without distorting. In contrast, square bars, lacking this axial symmetry, experience significant distortion across their cross-sections when subjected to torsion, with the exception of along their diagonals and at lines connecting midpoints. A detailed examination of a cubic element...
356