Thermodynamic Properties, Viscosity, and Structure of CaO-SiO2-MgO-Al2O3-TiO2-Based Slag

Jinle Fang1,2, Zhuogang Pang1, Xiangdong Xing1

  • 1School of Metallurgical Engineering, Xi'an University of Architecture and Technology, Xi'an 710055, China.

Materials (Basel, Switzerland)
|January 5, 2021
PubMed

Keywords:
activation energyenthalpy changeheat capacitystructureviscosityslag viscositythermodynamic propertiesTiO₂ effect on slagFTIR analysis of slag

More Related Videos

Reaction Kinetics and Combustion Dynamics of I4O9 and Aluminum Mixtures09:16

Reaction Kinetics and Combustion Dynamics of I4O9 and Aluminum Mixtures

Published on: November 7, 2016

11.2K
Synthesis and Characterization of Fe-doped Aluminosilicate Nanotubes with Enhanced Electron Conductive Properties09:34

Synthesis and Characterization of Fe-doped Aluminosilicate Nanotubes with Enhanced Electron Conductive Properties

Published on: November 15, 2016

9.5K

Related Concept Videos

Strength and Heat of Hydration01:29

Strength and Heat of Hydration

The hydration of cement is an exothermic reaction in which heat is generated as cement hydrates. This heat of hydration is critical to cement's strength development. The rate at which this heat is generated affects the temperature rise, with a majority of the heat being released early in the hydration process, half within the first three days, and about 75% within the first week.
The heat of hydration for each cement compound is significant; for instance, tricalcium aluminate (C3A) and...
480
Types of Cement II01:22

Types of Cement II

Portland blast-furnace cement is made by blending Portland cement clinker with granulated blast-furnace slag, which accounts for 25 to 65 percent of the cement's weight. Despite its similarities to ordinary Portland (Type I) cement in terms of fineness and setting times, its early strength is lower, though it achieves comparable strength later on. It's particularly suited for mass concrete structures and marine environments due to its lower heat of hydration and superior sulfate...
256
Transition Zone01:28

Transition Zone

The transition zone in concrete is a critical area where aggregate meets cement paste, marked by a distinct porosity and weakness compared to the surrounding material. The adhesion around the aggregates is primarily due to Van Der Waals forces. The voids within this zone influence its robustness; initially, it is less durable than the surrounding bulk mortar due to larger voids. Initially, when concrete is compacted, a higher water-cement ratio near the aggregates leads to the formation of...
230
Hydration of Cement01:24

Hydration of Cement

Hydration of cement is a chemical reaction between cement particles and water. This process occurs primarily through two mechanisms: through-solution and topochemical. In the through-solution process, anhydrous compounds dissolve into their constituents, hydrates form in the solution, and then precipitate from the supersaturated solution. The topochemical process involves solid-state reactions at the cement particle surface. The through-solution process dominates the topochemical process at the...
536