Ceramic hydroxyapatite foam as a new material for Bisphenol A removal from contaminated water

Ceramic hydroxyapatite foam (CF-HAP) was prepared by combining slip-casting and foaming methods. The prepared CF-HAP was characterized by scanning electron microscopy (SEM), physisorption of N₂, Fourier transforms infrared spectroscopy (FTIR), and X-ray diffraction (XRD). The results of the specific surface area and SEM analyses revealed that the used shaping method provides CF-HAP with a wide range of porosity including macro and mesopores. Based on FTIR and XRD analyses, the CF-HAP is similar to pure well-crystallized hydroxyapatite. The adsorption results revealed that 94% of the BPA with a concentration of (40 mg/L) was effectively removed from the water and that the maximum adsorption capacity was higher in acidic than in basic medium. The thermodynamic studies indicated that the adsorption reaction was spontaneous and endothermic in nature. The adsorption capacity increased with the temperature and the BPA is chemisorbed on the ceramic foam. The isotherm data fitted slightly better with the Liu than with the Freundlich and Langmuir models suggesting that the adsorption was homogeneous and occurred only in the monolayer. The adsorption process depends largely on the BPA concentration and the results fitted well with the pseudo-first-order model. This confirms that the interaction between the BPA and the CF-HAP was mainly chemical in nature. The FTIR analysis of the used and fresh CF-HAP showed that all the hydroxyl and phosphorus bands characteristic of the hydroxyapatite shifted after adsorption of Bisphenol A. This suggests that the adsorption of Bisphenol A occurred in the sites of the hydroxyapatite. Therefore, it can be concluded that the CF-HAP has the potential to be used as an adsorbent for wastewater treatment and purification processes.