π-Conjugated Chromophore Incorporated Polystyrene Nanobeads as Single Optical Agent for Three-Channel Fluorescent...

Fluorescent polystyrene (PS) nanobeads in the size range ∼70-120 nm incorporating perylene bisimide (PBI-PS) and/or oligo(p-phenylenevinylene) (OPV-PS) was developed by miniemulsion polymerization technique. A dye loading content (DLC) of <3% was sufficient to impart high fluorescence emission capability to the PS beads. OPV-PS exhibited emission in the range 400-550 nm with peak emission at 450 nm (λ_ex = 350 nm; ϕ_FL = 26%); PBI-PS showed emission from 520-650 nm with peak emission at 545 nm (λ_ex = 490 nm; ϕ_FL = 9.7%) in 1× PBS buffer, whereas OPV(PBI)-PS nanobeads incorporating both the fluorophores exhibited multicolor emission capabilities (λ_ex from 350 to 490 nm). The nanoparticles were characterized by field-emission scanning electron microscopy (FESEM), transmission electron microscopy (TEM) and dynamic light scattering (DLS) for size and zeta potential for surface charge. For bioimaging applications, the PS nanoparticles were incubated with HeLa cells. Cell viability analysis involving HeLa cells showed more than 90% cell viability confirming the biocompatibility of the PS beads. The cellular uptake of the nanoparticles was confirmed by flow cytometry analysis and confocal laser scanning microscopy (CLSM) images. The subcellular localization of the nanoparticles in the cytoplasm could be precisely established by their simultaneous multicolor emission. The PS-based single optical agent presented here that can function as three-channel fluorescent probe to meet the requirements for multicolor bioimaging is advantageous.