The effect of different liners on the bond strength of a compomer to primary teeth dentine: in vitro study
R Frankenberger1, S Nassiri2, S Lücker2
1Department of Operative Dentistry and Endodontics, Dental School, University of Marburg and University Medical Center Giessen and Marburg, Campus Marburg, Georg-Voigt-Str. 3, 35039, Marburg, Germany.
Objective:
This in vitro investigation should identify the effect of protective liners on dentine bond strength of a polyacid modified resin composite to dentine of primary teeth.
Methods:
Forty-two extracted caries-free primary molars were randomly assigned to seven groups (n = 6) and flattened. Six test groups were centrally covered with different protective liners/base materials: Kerr Life (KL), IRM zinc oxide eugenol cement (IRM), Ketac Bond (KB), Vitrebond (VB), Dycal (DY), and mineral trioxide aggregate (MTA). Specimens were bonded with Prime&Bond NT (PB) and restored with Dyract eXtra. The control group (C) did not receive liner pretreatment. After 24-h storage in Aqua dest. (37 °C), specimens were cut and regional microtensile bond strengths of the uncovered areas were tested. Fractography was conducted under a light microscope and further interface/surface analyses were performed under a SEM. Statistical appraisal was carried out using oneway ANOVA (mod. LSD test; p < 0.05).
Results:
Independent of the distance to the applied liner, all groups exhibited inferior μ-TBS to dentine of primary teeth compared to the control group (p < 0.05). The results were as follows in MPa(SD) x:significance level/percentage of adhesive fractures: PB: 34 (10)A/72%; KL: 23 (25)B/64%; KB: 15 (12)C/76%; DY 15 (13)C/55%; IRM: 14 (10)C/68%; VB: 12 (10)C/61%; MTA 12 (10)C/69%.
Conclusions:
Protective liners significantly reduced μ-TBS to dentine of primary teeth.
Related Concept Videos
01:12Bonding and Strength of Aggregate
01:20Strength of Cement
For compressive strength tests, ASTM C 109-05 standards prescribe a cement-sand mix ratio of 1:2.75 and a water/cement ratio of 0.485 for making 2-inch cubes. These cubes are mixed, cast, and cured in saturated lime water at 23°C until testing. Flexural strength testing, outlined in...
02:40Chemical Bonds
Atoms participate in a chemical bond formation to acquire a completed valence-shell electron configuration similar to that of the noble gas nearest to it in atomic number. Ionic, covalent, and metallic bonds are some of the important types of chemical bonds. Bond energy and bond length determine the strength of a chemical bond.
Types of Chemical Bonds
An ionic bond is formed due to electrostatic attraction between cations and anions. Often, the ions are formed by the transfer of electrons...