Functionalization Mechanism of Reduced Graphene Oxide Flakes with BF3·THF and Its Influence on Interaction with Li+
Łukasz Kaczmarek1, Magdalena Balik1, Tomasz Warga1
1Institute of Materials Science and Engineering, Lodz University of Technology, Stefanowskiego 1/15, 90-924 Lodz, Poland.
Abstract:
Doping of graphene and a controlled induction of disturbances in the graphene lattice allows the production of numerous active sites for lithium ions on the surface and edges of graphene nanolayers and improvement of the functionality of the material in lithium-ion batteries (LIBs). This work presents the process of introducing boron and fluorine atoms into the structure of the reduced graphene during hydrothermal reaction with boron fluoride tetrahydrofuran (BF3·THF). The described process is a simple, one-step synthesis with little to no side products. The synthesized materials showed an irregular, porous structure, with an average pore size of 3.44-3.61 nm (total pore volume (BJH)) and a multi-layer structure and a developed specific surface area at the level of 586-660 m2/g (analysis of specific surface Area (BET)). On the external surfaces, the occurrence of irregular particles with a size of 0.5 to 10 µm was observed, most probably the effect of doping the graphene structure and the formation of sp3 hybridization defects. The obtained materials show the ability to store electric charge due to the development of the specific surface area. Based on cyclic voltammetry, the tested material showed a capacity of 450-550 mAh/g (charged up to 2.5 V).
More Related Videos
10:41The Effect of Charging and Discharging Lithium Iron Phosphate-graphite Cells at Different Temperatures on Degradation
Published on: July 18, 2018
11:25Identification and Quantification of Decomposition Mechanisms in Lithium-Ion Batteries; Input to Heat Flow Simulation for Modeling Thermal Runaway
Published on: March 7, 2022
Related Concept Videos
01:19Acid Halides to Alcohols: LiAlH4 Reduction
The mechanism proceeds in three steps. First, the nucleophilic hydride ion attacks the carbonyl carbon of the acid halide to form a tetrahedral intermediate. Next, the carbonyl group is re-formed, and the halide ion departs as a leaving group, generating an aldehyde. A second nucleophilic attack by the hydride yields an alkoxide ion, which, upon protonation, gives a primary alcohol as...
02:23Alcohols from Carbonyl Compounds: Reduction
Catalytic hydrogenation is similar to the reduction of an alkene or alkyne by adding H2 across the pi bond in the presence of transition metal catalysts like Raney Ni, Pd–C, Pt, or Ru. Aldehydes and ketones can be reduced by this method, often under mild to moderate heat (25–100°C) and...
01:17Carboxylic Acids to Primary Alcohols: Hydride Reduction
01:17Esters to Alcohols: Hydride Reductions
Lithium aluminum hydride is a source of hydride ions and functions as a nucleophile. The mechanism proceeds in three steps. Firstly, the nucleophilic hydride ion attacks the carbonyl carbon of the ester to form a tetrahedral intermediate. Subsequently, the carbonyl group re-forms,...
02:48Ionic Bonding and Electron Transfer
00:55Nitriles to Amines: LiAlH4 Reduction
As shown below, the mechanism involves three steps. Firstly, the hydride ion acting as a nucleophile attacks the nitrile carbon to form an anion. In the second step, a second equivalent of the hydride ion attacks the anion to...