Hierarchically Demineralized Cortical Bone Combined With Stem Cell-Derived Extracellular Matrix for Regeneration of...

Poor healing of the tendon-bone interface after rotator cuff repair is one of the main causes of surgical failure. Previous studies demonstrated that demineralized cortical bone (DCB) could improve healing of the enthesis.

To evaluate the outcomes of hierarchically demineralized cortical bone (hDCB) coated with stem cell-derived extracellular matrix (hDCB-ECM) in the repair of the rotator cuff in a rabbit model.

Controlled laboratory study.

Tendon-derived stem cells (TDSCs) were isolated, cultured, and identified. Then, hDCB was prepared by the graded demineralization procedure. Finally, hDCB-ECM was fabricated via 2-week cell culture and decellularization, and the morphologic features and biochemical compositions of the hDCB-ECM were evaluated. A total of 24 rabbits (48 samples) were randomly divided into 4 groups: control, DCB, hDCB, and hDCB-ECM. All rabbits underwent bilateral detachment of the infraspinatus tendon, and the tendon-bone interface was repaired with or without scaffolds. After surgery, 8 rabbits were assessed by immunofluorescence staining at 2 weeks, and the others were assessed by micro-computed tomography (CT) examination, immunohistochemical staining, histological staining, and biomechanical testing at 12 weeks.

TDSCs were identified to have universal stem cell characteristics including cell markers, clonogenicity, and multilineage differentiation. The hDCB-ECM contained 3 components (bone, partial DCB, and DCB coated with ECM) with a gradient of calcium and phosphorus elements, and the ECM had stromal cell-derived factor 1, biglycan, and fibromodulin. Macroscopic observations demonstrated the absence of infection and rupture around the enthesis. The results of immunofluorescence staining showed that hDCB-ECM promoted stromal cell recruitment. Results of micro-CT analysis, immunohistochemical staining, and histological staining showed that hDCB-ECM enhanced bone and fibrocartilage formation at the tendon-bone interface. Biomechanical analysis showed that the hDCB-ECM group had higher ultimate tensile stress and Young modulus than the DCB group.

The administration of hDCB-ECM promoted healing of the tendon-bone interface.

hDCB-ECM could provide useful information for the design of scaffolds to repair the tendon-bone interface, and further studies are needed to determine its effectiveness.