Ion irradiation induced strain and structural changes in LiTaO₃perovskite

LiTaO₃crystals irradiated with 3 MeV and 1.162 GeV Au ions were studied by single crystal x-ray diffraction and Raman scattering measurements. The maximum lattice strains after 3 MeV Au ion irradiation to a fluence of 1.2 × 10¹³ cm^-2were 1.2% and 0.6% along thec- anda-/b-axes, respectively. Two effects were observed in 1.162 GeV Au ion irradiated samples: (i) the (0006) and (1120) Bragg peaks were split into doublets, which suggested a subtle structural change due to slight modification of chemical composition; and (ii) the pre-damaged 1.2% lattice strain along thec-axis was relaxed to 0.9% after subsequent irradiation with 1.162 GeV Au ions, while relaxation along thea- orb-axis was not obvious. A distinct change in the Raman spectrum of the 〈0001〉 oriented LiTaO₃crystals was observed after 1.162 GeV Au ion irradiation, but no obvious change was observed in the 〈1120〉 oriented samples or in 3 MeV Au ion irradiated samples. Strain and structural changes in crystalline LiTaO₃, with or without pre-existing defects, upon ion irradiation are delineated in its responding to inelastic ionization and elastic nuclear collisions.