Determination of Hafnium Zirconium Oxide Interfacial Band Alignments Using Internal Photoemission Spectroscopy and
Melanie A Jenkins1, Konner E K Holden1, Sean W Smith2
1School of Electrical Engineering and Computer Science, Oregon State University, Corvallis, Oregon 97330, United States.
Abstract:
Doped ferroelectric HfO2 is highly promising for integration into complementary metal-oxide semiconductor (CMOS) technology for devices such as ferroelectric nonvolatile memory and low-power field-effect transistors (FETs). We report the direct measurement of the energy barriers between various metal electrodes (Pt, Au, Ta, TaN, Ti/Pt, Ni, Al) and hafnium zirconium oxide (Hf0.58Zr0.42O2, HZO) using internal photoemission (IPE) spectroscopy. Results are compared with valence band offsets determined using the three-sample X-ray photoelectron spectroscopy (XPS) as well as the two-sample hard X-ray photoelectron spectroscopy (HAXPES) techniques. Both XPS and IPE indicate roughly the same dependence of the HZO barrier on metal work function with a slope of 0.8 ± 0.5. XPS and HAXPES-derived barrier heights are on average about 1.1 eV smaller than barrier heights determined by IPE, suggesting the presence of negative charge in the HZO.