Increased structural defects of graphene oxide compromised reductive capacity of ZVI towards hexavalent chromium

Graphene oxide (GO) was treated with irradiation beams to understand the defective degree of carbon structure of GO in relation to electron transfer property of impregnated zerovalent iron (ZVI). The GO-supported ZVI (ZVI/GO) was synthesized and then characterized by an X-ray diffraction (XRD), X-ray photoelectron spectroscopy (XPS), Fourier transform infrared spectroscopy (FTIR) and Raman spectroscopy. The results showed that the oxygen-bearing functional groups, oxygen content and structural disorder were increased as a function of irradiation beam intensity. ZVI was dominant in the composites, but proportion of iron oxide increased with greater oxygen content. Batch sorption revealed that Cr(VI) removal decreased from 20.11 g kg^-1 to 2.30 g kg^-1 as solution pH rose from 3 to 9. Cr(VI) removal capacity was 26.39 g kg^-1, 23.12 g kg^-1 and 12.35 g kg^-1 for ZVI/GO₀, ZVI/GO_12.3 and ZVI/GO_36.9, respectively. The reduction capacity of sorbents followed similar trends as Cr(VI) sorption as per desorption experiment, which accounted for a major Cr(VI) detoxification mechanism by ZVI/GO composites. The electrochemical tests demonstrated that unfavorable electron transfer rate of ZVI/GO composites was aggravated by greater structural disorder of GO. Thus, higher dose of irradiations could create more disorder in graphitic carbon and promote oxidation of ZVI, which hindered Cr(VI) reduction.