Crystalline carbon modified hierarchical porous iron and nitrogen co-doped carbon for efficient electrocatalytic
Shanfu Sun1, Zhiyuan Yin1, Bowen Cong1
1MIIT Key Laboratory of Critical Materials Technology for New Energy Conversion and Storage, School of Chemistry and Chemical Engineering, Harbin Institute of Technology, Harbin 150001, PR China.
Abstract:
Hierarchical porous iron and nitrogen co-doped carbon (Fe-N/C) materials have been considered as an appealing non-noble metal-based catalyst in oxygen reduction reactions (ORR). However, the conductivity loss caused by the scattering of electrons on pores and defects markedly limits their catalytic activity, which attracted seldom attention in this area. Herein, a novel crystalline carbon modified hierarchical porous Fe-N/C electrocatalyst with enhanced electronic conductivity is designed and prepared via a two-step calcination-catalysis process. The resistivity of hierarchical porous Fe-N/C is decreased from 2.123 Ω cm to 0.479 Ω cm after crystalline carbon introduction. The electrocatalyst annealed at 800 °C (Fe-N/C-800) exhibits a superior activity with the half-wave potential (E1/2) of 0.89 V, which outperforms the commercial carbon-supported platinum (Pt/C) catalyst (0.85 V). The strategy of crystalline carbon modification provides a fresh approach to improve the electronic conductivity of porous carbon-based materials.