Quantification Approaches for Fatigue Crack Resistance of Thermoplastic Tape Layered Composites with Multiple...

Automated tape placement with in-situ consolidation (ATPisc) is a layer-wise manufacturing process in which the achievement of proper interlayer bonding constitutes one of the most challenging aspects. In the present study, unidirectional carbon fiber reinforced thermoplastic laminates were produced following different manufacturing protocols using ATPisc. The interlayer bonding of the laminates produced was characterized by mode I fatigue fracture tests with double cantilever beam (DCB) specimens. Independent of the manufacturing approach, the laminates exhibited multiple cracking during DCB testing, which could not be evaluated simply following standard methods. Thus, various data analysis methodologies from literature were applied for the quantitative assessment of the fracture behavior of the laminate. The examination of the evolution of the damage parameter φ and the effective flexural modulus throughout testing enabled a better understanding of the damage accumulation. The Hartman-Schijve based approach was revealed to be a convenient method to present fatigue crack growth curves of laminates with multiple delaminations. Moreover, a preliminary attempt was made to employ a 'zero-fiber bridging' methodology to eliminate the effect of additional damage processes on the fatigue crack growth that resulted in large-scale, partially massive fiber bridging.