Influence of Corrosion on Fatigue of the Fastening Bolts

Maciej B Lachowicz1,2, Marzena M Lachowicz1

  • 1Department of Metal Forming, Welding Technology and Metrology, Faculty of Mechanical Engineering, Wroclaw University of Science and Technology, Lukasiewicza 7-9, 50-371 Wroclaw, Poland.

Materials (Basel, Switzerland)
|April 3, 2021
PubMed

Keywords:
corrosionfastenersfatigue failuregalvanized boltshigh strength boltsthread roots cracking

More Related Videos

Determining Tribocorrosion Rate and Wear-Corrosion Synergy of Bulk and Thin Film Aluminum Alloys07:12

Determining Tribocorrosion Rate and Wear-Corrosion Synergy of Bulk and Thin Film Aluminum Alloys

Published on: September 11, 2018

11.6K
Full-field Strain Measurements for Microstructurally Small Fatigue Crack Propagation Using Digital Image Correlation Method07:37

Full-field Strain Measurements for Microstructurally Small Fatigue Crack Propagation Using Digital Image Correlation Method

Published on: January 16, 2019

9.9K

Related Concept Videos

Fatigue01:21

Fatigue

Fatigue occurs when materials rupture under repeated or fluctuating loads, even at stress levels far below their static breaking strength. It typically results in brittle failure, even for ductile materials. It is a critical consideration in designing machines and structural components subjected to repetitive or varying loads. The nature of these loadings can range from fluctuating loads like unbalanced pump impellers causing vibrations to repeatedly bending a thin steel rod wire back and forth...
355
Corrosion of Reinforcement01:27

Corrosion of Reinforcement

The corrosion of steel reinforcement within concrete is a process influenced by the material's inherent properties and external factors. The high pH level of around 13, provided by calcium hydroxide present in concrete, initially protects the steel reinforcement by promoting the formation of a passive iron oxide layer on its surface.
However, over time and under certain conditions like carbonation, chloride ingress, and cracking this protective state can be compromised. Steel has areas with...
362
Fatigue Strength of Concrete01:22

Fatigue Strength of Concrete

Fatigue, in the context of materials science and engineering, refers to the weakening or failure of a material caused by repeatedly applied loads, even if these loads are below the strength limit of the material. Fatigue strength in concrete is a critical property that influences its durability and longevity. Concrete can fail in two ways due to fatigue. Static fatigue or creep rupture occurs under a constant load or one that increases slowly. The other failure mode is due to cyclical or...
367
Steel Fastening Techniques01:17

Steel Fastening Techniques

Steel sections can be joined together through various fastening techniques including riveting, bolting, and welding, each suitable for different structural requirements and conditions.
Rivets are cylindrical steel fasteners with a specially designed head. During application, rivets are heated until white-hot and then inserted through pre-drilled holes in the steel sections. A pneumatic hammer is used to shape the exposed end into a second head, securing the sections together.
Bolting is another...
427
Corrosion02:49

Corrosion

The degradation of metals due to natural electrochemical processes is known as corrosion. Rust formation on iron, tarnishing of silver, and the blue-green patina that develops on copper are examples of corrosion. Corrosion involves the oxidation of metals. Sometimes it is protective, such as the oxidation of copper or aluminum, wherein a protective layer of metal oxide or its derivatives forms on the surface, protecting the underlying metal from further oxidation. In other cases, corrosion is...
26.9K
Wood Fasteners01:18

Wood Fasteners

In wood construction, fasteners are essential for securing components together, with the connection strength largely dependent on the direct bearing between members. Various types of fasteners are employed, each suited to specific applications and structural requirements.
Nails are the most common fasteners, consisting of sharp-pointed metal pins that are driven into wood using a hammer or a mechanical nail gun. They come in a variety of diameters, heads, and lengths. Nailing techniques include...