Effect of layer thickness on the elution of monomers from two high viscosity bulk-fill composites: A high-performance...

The aim is to evaluate the effect of different layer thickness on the amount of elution of monomers from two high viscosity bulk-fill composites after 24 h and 1 month storage in ethanol using high-performance liquid chromatography (HPLC) analysis.

Forty-eight samples prepared from two high viscosity bulk-fill composite resins; Tetric EvoCeram Bulk Fill and x-tra fil were divided into three groups (n = 8) based on their layer thickness, i.e., Group 1 (2 mm), Group 2 (4 mm), and Group 3 (6 mm) and were then subdivided based on their storage period. The analysis of the eluates was performed using HPLC unit. Statistical analysis was performed using One-way ANOVA, independent sample t-test, and paired "t" test at a significance level of 0.05 (P < 0.05).

Increase in layer thickness resulted in increased amount of bisphenol A-glycidyl methacrylate (Bis-GMA) and urethane dimethacrylate (UDMA) elution for both composites, i.e., Group 3 > Group 2 > Group 1 and there was statistically significant difference among all the groups. Tetric EvoCeram Bulk Fill showed a statistically significant increase in amount of Bis-GMA and UDMA elution for all groups compared to x-tra fil. Furthermore, increase in storage period resulted in statistically significant increase in amount of Bis-GMA and UDMA elution for both composites, i.e., Group 1B > Group 1A, Group 2B > Group 2A, and Group 3B > Group 3A. The mean value of UDMA elution was higher when compared to that of Bis-GMA elution for both composites and there was statistically significant difference for all groups.

Within the limitations of this in vitro study, it was concluded that increase in layer thickness resulted in increased amount of Bis-GMA and UDMA elution for both Tetric EvoCeram Bulk Fill and x-tra fil.