Magnetically Assembled Photonic Crystal Gels with Wide Thermochromic Range and High Sensitivity

Thermochromic poly(N-isopropyl acrylamide) (PNIPAM) photonic crystal gels based on 1D magnetically assembling colloidal nanocrystal clusters have attracted much attention due to its convenient preparation process, striking color response, and good mechanical strength. However, there remain challenges to broaden the thermochromic range and improve the sensitivity for their iridescent color display. Here, a PNIPAM photonic gel with wide thermochromic range and high sensitivity is prepared by using four-arm star poly(ethylene glycol) acrylamide (PEGAAm) as cross-linker at appropriately reduced magnetic field strength as well as cross-linker content. PEGAAm improves the homogeneity of the microstructure in PNIPAM photonic gel and thus maintains the structure colors at a wide temperature range from room temperature to 44 °C. The reduced magnetic field strength of 70 Gs and low cross-linker content (the molar ratio of monomer to cross-linker of 300:1) lead to a large initial lattice spacing of the photonic gel and thus wide diffraction wavelength migration of 194 nm. This optimized PNIPAM gel exhibits vivid iridescent colors from orange-red to indigo blue as temperature increases from 20 to 44 °C with satisfactory repeatability. Therefore, it may be an ideal candidate for temperature sensors and displays with utility and accuracy such as low-temperature burns.