Effect of Martensite Volume Fraction on Oxidative and Adhesive Wear

Yunbo Zhang1, Abdeljalil Jourani1

  • 1FRE UTC-CNRS 2012 Roberval, Université de Technologie de Compiègne, Alliance Sorbonne Université, Centre de Recherche Royallieu, CS 60 319, CEDEX, 60 203 Compiègne, France.

Materials (Basel, Switzerland)
|June 2, 2021
PubMed

Keywords:
adhesive weardual phasesfrictionmicrostructureoxidative wear

More Related Videos

Preparation and High-temperature Anti-adhesion Behavior of a Slippery Surface on Stainless Steel10:52

Preparation and High-temperature Anti-adhesion Behavior of a Slippery Surface on Stainless Steel

Published on: March 29, 2018

7.8K
Experimental Multiscale Methodology for Predicting Material Fouling Resistance09:13

Experimental Multiscale Methodology for Predicting Material Fouling Resistance

1.5K

Related Concept Videos

Abrasion Resistance of Concrete01:23

Abrasion Resistance of Concrete

Abrasion resistance is an essential characteristic of concrete that determines its durability and longevity under various wear conditions. Concrete surfaces are vulnerable to different types of abrasion. For instance, surfaces may wear down due to the constant movement of vehicles or be eroded by solids carried in water, as seen in concrete canal linings. Specific tests are conducted to measure the abrasion resistance of concrete.
One such test is the revolving disc test, where three plates...
290
Oxidation of Alkenes: Syn Dihydroxylation with Osmium Tetraoxide02:44

Oxidation of Alkenes: Syn Dihydroxylation with Osmium Tetraoxide

Alkenes are converted to 1,2-diols or glycols through a process called dihydroxylation. It involves the addition of two hydroxyl groups across the double bond with two different stereochemical approaches, namely anti and syn. Dihydroxylation using osmium tetroxide progresses with syn stereochemistry.
11.3K
Oxidation of Alkenes: Anti Dihydroxylation with Peroxy Acids02:04

Oxidation of Alkenes: Anti Dihydroxylation with Peroxy Acids

Diols are compounds with two hydroxyl groups. In addition to syn dihydroxylation, diols can also be synthesized through the process of anti dihydroxylation. The process involves treating an alkene with a peroxycarboxylic acid to form an epoxide. Epoxides are highly strained three-membered rings with oxygen and two carbons occupying the corners of an equilateral triangle. This step is followed by ring-opening of the epoxide in the presence of an aqueous acid to give a trans diol.
6.4K
Radical Oxidation of Allylic and Benzylic Alcohols01:21

Radical Oxidation of Allylic and Benzylic Alcohols

Activated manganese(IV) oxide can selectively oxidize allylic and benzylic alcohols via a radical intermediate mechanism. Primary allylic alcohols are oxidized to aldehydes, while secondary allylic alcohols yield ketones. The redox reaction of potassium permanganate with an Mn(II) salt such as manganese sulfate (under either alkaline or acidic conditions), followed by thorough drying, yields the oxidizing agent: activated MnO2. While MnO2 is insoluble in the solvents used for the reaction, the...
2.5K
Frictional Force01:07

Frictional Force

When a body is in motion, it encounters resistance because the body interacts with its surroundings. This resistance is known as friction, a common yet complex force whose behavior is still not completely understood. Friction opposes relative motion between systems in contact, but also allows us to move. Friction arises in part due to the roughness of surfaces in contact. For one object to move along a surface, it must rise to where the peaks of the surface can skip along the bottom of the...
8.9K
Oxidation of Alkenes: Syn Dihydroxylation with Potassium Permanganate02:21

Oxidation of Alkenes: Syn Dihydroxylation with Potassium Permanganate

Alkenes can be dihydroxylated using potassium permanganate.  The method encompasses the reaction of an alkene with a cold, dilute solution of potassium permanganate under basic conditions to form a cis-diol along with a brown precipitate of manganese dioxide.
14.3K