Thickness-Dependent Permeance of Molecular Layer-By-Layer Polyamide Membranes

We present the thickness-dependent permeance of highly cross-linked polyamide (PA) membranes formed by a molecular layer-by-layer (mLbL) deposition process. The deposition allows for the synthesis of extremely smooth, uniform PA films of tunable thickness, which is counter to the less controlled interfacial polymerization process used commercially. The ability to control and measure the membrane thickness allows us to elucidate the relationships among network structure, transport properties, and separation performance. In this work, a series of large-area mLbL PA membranes is prepared with thickness ranging from less than 5 nm to greater than 100 nm, which can be transferred defect-free via a film floating technique onto a macroporous support layer and challenged with salt solutions. A critical thickness of 15 nm is identified for efficient desalination, and water permeance is described using a multi-layer solution diffusion model that allows for the extraction of material properties relevant to transport. Finally, the model demonstrates the existence of two distinct layers in the mLbL films, one layer comprised of a (5 to 10) nm graded or less cross-linked layer at the surface and a more densely cross-linked layer in the interior of the film. This graded layer appears inherent to the mLbL deposition process and is observed at all film thicknesses.