Preparation of covalently bonded silica-alginate hybrid hydrogels by SCHIFF base and sol-gel reactions

Organic-inorganic hybrid materials overcome drawbacks associated with alginate hydrogels. In this work, covalently coupled silica-alginate hybrids were prepared by Schiff base formation and sol-gel reaction using alginate dialdehyde (ADA), (3-Aminopropyl) triethoxysilane (APTES), and APTES/tetraethylorthosilicate (TEOS) precursors. The influence of the polysaccharide/inorganic ratio, the nature of the inorganic precursor and the ionic crosslinking ability are studied. Prepared hybrids were characterized by FT-IR, ¹³C and ²⁹Si NMR spectroscopies, SEM, and rheology. For ADA/APTES hybrids, at higher ADA content, Schiff base formation is predominant, but at lower ADA content, the sol-gel reaction is prevalent. However, the progress of the sol-gel reactions for ADA/(APTES+TEOS), is favored with higher ADA compositions. Introducing a posterior ionic crosslinking treatment was possible, increasing the moduli in ADA/(APTES+TEOS) hybrids from 86,207 Pa for 1.5 ADA/Si to 362,171 Pa for 1.5 ADA/Si-Ca. In-situ ADA-Silica hybrid hydrogels containing both ionic and covalent crosslinking can be successfully synthesized with the proposed method. CARBPOL-D-21-01042.