Biodegradable phase change materials with high latent heat: Preparation and application on Lentinus edodes storage
Qi Kong1, Honglei Mu1, Yanchao Han1
1Food Science Institute, Zhejiang Academy of Agricultural Sciences, Key Laboratory of Post-Harvest Handing of Fruits, Ministry of Agriculture and Rural Affairs, Key Laboratory of Fruits and Vegetables Postharvest and Processing Technology Research of Zhejiang Province, Key Laboratory of Postharvest Preservation and Processing of Fruits and Vegetables, China National Light Industry, Hangzhou 310021, China.
None:
In order to develop biodegradable phase change materials (PCMs) with high latent heat for cold chain logistics, superabsorbent resin (SAR) was prepared based on starch graft copolymerization. FTIR and DSC demonstrated that acrylic acid was successfully grafted onto starches and optimum latent heat of PCM was 330.4 J/g with 10% (w/w) starch. The water retention of PCM with 10% (w/w) starch was 0.49 after heating at 50 °C for 200 h, which was 4.9 folds higher than that of non-starch PCM. Biodegradation rate of PCM was 60.12% within 75-day burial, which was 6 folds higher than that of non-starch PCM. Moreover, significant reduction in browning index, odor, decay, relative conductivity and malondialdehyde (MDA) content was observed in Lentinus edodes treated by biodegradable PCM. These results indicated that the application of biodegradable PCM could extend the shelf life of fresh L. edodes stored at 25 °C.