Analysis of Microstructure and Mechanical Properties of AlSi11 after Chip Recycling, Co-Extrusion, and Arc Welding

Recycling of raw materials and is crucial for the production of new products for the global economy. The aim here is, on the one hand, to reduce energy consumption, and, on the other hand, to obtain materials with similar functional properties. The study undertook research on the possibility of processing AlSi11 aluminum chips by compaction and co-extruding to obtain a product in the form of a flat bar with mechanical properties not lower than those of the cast materials. The performed tests and the developed technique allowed to obtain flat bars with more favorable mechanical properties (Yield Strength YS ≥ 155 MPa; Ultimate Tensile Strength UTS ≥ 212 MPa) than the castings (YS ≥ 70 MPa ≥ 150 MPa). The weldability evaluation tests revealed that the material is susceptible to porosity. The presence of pores, which reduces the cross-section (up to 60%), reduces the tensile strength (up to 20 MPa). The typical joint structure and plasticity is obtained, which indicate the possibility of tensile strength improvement.