Preparation of Expanded Graphite and Graphite Nanosheets for Improving Electrical Conductivity of Polyester Coating...

Expanded graphite and graphite nanosheets were facilely prepared by the thermal expansion of expandable graphite at 800 °C and sand milling of expanded graphite in water, respectively. When the expandable graphite precursor was prepared by the oxidation and intercalation of natural graphite (5 g) using KMnO₄ (6 g) as an oxidant in a concentrated sulfuric acid solution (120 mL) at room temperature (25 °C) for 8 h, the expanded graphite with a maximum volumetric rate of 317 mL g^-1 was prepared after the thermal expansion of the expandable graphite precursor at 800 °C for 60 s. The oxidation extent of natural graphite with KMnO₄ is crucial for the preparation of expanded graphite. The thicknesses of graphite nanosheets decreased from 8.9 to 3.2 nm when the sand milling time of the expanded graphite in deionized water was prolonged from 6 to 24 h. The prolonging of the sand milling time not only decreased the layer number of the graphite nanosheet but also increased the d₀₀₂ spacing due to the shocking and shearing forces. The addition of the expanded graphite powder and graphite nanosheets in a polyester paint efficiently improved the electrical conductivity of the resultant polyester coating films.