Nanosecond Laser Cleaning Method to Reduce the Surface Inert Layer and Activate the Garnet Electrolyte for a...

The garnet-type electrolyte Li_6.4La₃Zr_1.4Ta_0.6O₁₂ (LLZTO) has been widely researched for its high ionic conductivity and excellent stability against the Li anode. However, the garnet electrolyte is susceptible to CO₂ and H₂O in air to form a Li₂CO₃ insulating layer leading to poor wettability with the Li anode, which hinders its practical application. Herein, we introduced a simple method to effectively reduce the Li₂CO₃ layer on the garnet electrolyte surface by laser cleaning and made the garnet surface back with lithiophilicity. The resulting Li/garnet interfacial resistance decreased to 76.4 Ω·cm² at 30 °C and 3.1 Ω·cm² at 80 °C. The assembled Li symmetric cell with the as-laser-treated electrolyte steadily cycled for 300 h under 0.1 and 0.2 mA·cm^-2 at 80 °C. The solid-state battery coupled with the composite LiFePO₄ cathode and the Li anode exhibited stable long-term cycling performance for over 100 cycles with a capacity retention of 84.8%. This work provided a novel method to reduce the surface inert layer and make the garnet electrolyte reveal the intrinsic lithiophilicity by laser cleaning process with high efficiency, which helped address the challenges for the application of garnet-based solid-state batteries.