Adsorption of benzene and toluene from aqueous solution using a composite hydrogel of alginate-grafted with...

Hydrogels are often claimed as optimal adsorbents for water treatment; however, their efficiency towards the removal of hydrophobic pollutants is still limited. As an alternative, hydrogels prepared from polymers functionalized with siliceous materials can overcome this issue. Here, a composite hydrogel (denoted as GEL-SBA15) was prepared using alginate grafted with mesoporous silica (SBA15) and poly(vinyl alcohol) for benzene and toluene adsorption from aqueous solutions. Adsorption studies demonstrated that a low dosage of GEL-SBA15 (10 mg) has a high adsorption capacity for benzene (1482.8 mg/g) and toluene (596.6 mg/g) under mild experimental conditions (pH 7.0, at 25 °C). Besides, the adsorption capacities of GEL-SBA15 for both pollutants were enhanced compared to the conventional hydrogel. Kinetic analysis showed that the adsorption of benzene and toluene follows a pseudo-second order model, while the experimental adsorption data were well-fitted by the Freundlich isotherm. According to this isotherm, the adsorption occurs via a collaborative process, and weak physical forces (π-π interactions, van der Waals and hydrophobic) are involved. Hence, the post-utilized GEL-SBA15 can be recycled and reused up to 6 times without losing adsorption performance. Although hydrogels are not common adsorbents for aromatic hydrocarbons, the results reported here rank GEL-SBA15 as a promising adsorbent for the removal of these pollutants from water.