Author Spotlight: A Rapid, Microwave-Assisted Hydrothermal Synthesis Of Nickel Hydroxide Nanosheets
Published on: August 18, 2023
NiFe Layered-Double-Hydroxide Nanosheet Arrays on Graphite Felt: A 3D Electrocatalyst for Highly Efficient Water
Peng Ding1,2, Chuqian Meng1, Jie Liang1
1Institute of Fundamental and Frontier Sciences, University of Electronic Science and Technology of China, Chengdu 610054, China.
Abstract:
It is of great importance to rationally design and develop earth-abundant nanocatalysts for high-efficiency water electrolysis. Herein, NiFe layered double hydroxide was in situ grown hydrothermally on a 3D graphite felt (NiFe LDH/GF) as a high-efficiency catalyst in facilitating the oxygen evolution reaction (OER). In 1.0 M KOH, NiFe LDH/GF requires a low overpotential of 214 mV to deliver a geometric current density of 50 mA cm-2 (η50 mA cm = 214 mV), surpassing that NiFe LDH supported on a 2D graphite paper (NiFe LDH/GP; η50 mA cm = 301 mV). More importantly, NiFe LDH/GF shows good durability at 50 mA cm-2 within 50 h of OER catalysis testing and delivers a faradaic efficiency of nearly 100% in the electrocatalysis of OER.
More Related Videos
08:40Synthesis of Metal Nanoparticles Supported on Carbon Nanotube with Doped Co and N Atoms and its Catalytic Applications in Hydrogen Production
Published on: December 6, 2021
10:57Synthesis and Performance Characterizations of Transition Metal Single Atom Catalyst for Electrochemical CO2 Reduction
Published on: April 10, 2018