Biodegradability of polyethylene mulching film by two Pseudomonas bacteria and their potential degradation mechanism

Wasted polyethylene (PE) products caused pollution has become a global issue. Researchers have identified PE-degrading bacteria which have been considered as a sustainable alleviation to this crisis. However, the degradation mechanism employed by currently isolated bacteria is unclear and their degradation efficiencies are insufficient. More importantly, there is little research into bacteria capable of degrading PE mulching film to solve "white" pollution in agriculture. We determined the PE degradation efficiency of two Pseudomonas, identified by 16S rDNA analysis, and elucidated their potential mechanisms through whole genome sequencing. During an 8-week period, PE mulch lost 5.95 ± 0.03% and 3.62 ± 0.32% of its mass after incubated with P. knackmussii N1-2 and P. aeruginosa RD1-3 strains, respectively. Moreover, considerable pits and wrinkles were observed on PE.The hydrophobicity of PE films also decreased, and new oxygenic functional groups were detected on PE mulch by Fourier Transform Infrared Spectrometry (FTIR). Complete genome sequencing analysis indicated that two Pseudomonas strains encode genes for enzymes and metabolism pathways involved in PE degradation. The results provide a theoretical basis for further research that investigates the mechanism driving the degradation and metabolism of discarded PE in the environment.