Ag-In-Zn-S Quantum Dot-Dominated Interface Kinetics in Ag-In-Zn-S/NiFe LDH Composites toward Efficient Photoassisted...

Photoassisted electrocatalysis (P-EC) emerges as a rising star for hydrogen production by embedding photoactive species in electrocatalysts, for which the interfacial structure design and charge transfer kinetics of the multifunctional catalysts remain a great challenge. Herein, Zn-AgIn₅S₈ quantum dots (ZAIS QDs) were embedded into 2D NiFe layered double hydroxide nanosheets through a simple hydrothermal treatment to form 0D/2D composite catalysts for P-EC. With evidence from transient photovoltage spectroscopy, we acquired a clear and fundamental understanding on the kinetics of charge extraction time and extraction amount in the 0D/2D heterojunctions that was proved to play a key role in P-EC. Upon light illumination, for HER, the optimized NiFe-ZAIS exhibits obviously reduced overpotentials of 129 and 242 mV at current densities of 10 and 50 mA cm^-2, which are 22 and 33 mV lower than those of dark electrocatalysis, respectively. For OER, the NiFe-ZAIS electrode also shows low overpotentials of 220 and 268 mV at current densities of 10 and 50 mA cm^-2, respectively, under light illumination, which were able to almost double the intrinsic activity. Finally, with NF@NiFe-ZAIS as both the cathode and the anode, the assembled electrolyzer only requires 1.62 V to reach the overall water splitting current density of 10 mA cm^-2 under P-EC. This work provides a useful example for the profound understanding of the design and the kinetics study of multifunctional P-EC catalysts.