Effect of Direct Powder Forging Process on the Mechanical Properties and Microstructural of Ti-6Al-4V ELI

The study of powder metallurgy processing methods for titanium represents a promising avenue that can respond to a growing demand. This work reports the feasibility of direct powder forging (DPF) as a method to process large spherical Ti-6Al-4V powder into wrought products with noteworthy properties and physical characteristics. Direct powder forging is a thermomechanical process that imparts uniaxial loading to an enclosed and uncompacted powder to produce parts of various sizes and shapes. Stainless steel canisters were filled with prealloyed Ti-6Al-4V powder and consolidated through a multi-step open-die forging and rolling process into wrought DPF bars. After DPF, annealing was performed in the upper α+β phase. The results show that full consolidation was achieved and higher mechanical properties than the Ti-6Al-4V grade F-23 requirements in annealed conditions were obtained. The results also show that direct powder forging of spherical titanium powder could produce wrought mill products and exhibit some potential for further investigation for industrial applications.