In Situ Synchrotron X-ray Diffraction Studies of Hydrogen-Desorption Properties of 2LiBH₄-Mg₂FeH₆ Composite

Adding a secondary complex metal hydride can either kinetically or thermodynamically facilitate dehydrogenation reactions. Adding Mg₂FeH₆ to LiBH₄ is energetically favoured, since FeB and MgB₂ are formed as stable intermediate compounds during dehydrogenation reactions. Such "hydride destabilisation" enhances H₂-release thermodynamics from H₂-storage materials. Samples of the LiBH₄ and Mg₂FeH₆ with a 2:1 molar ratio were mixed and decomposed under three different conditions (dynamic decomposition under vacuum, dynamic decomposition under a hydrogen atmosphere, and isothermal decomposition). In situ synchrotron X-ray diffraction results revealed the influence of decomposition conditions on the selected reaction path. Dynamic decomposition of Mg₂FeH₆-LiBH₄ under vacuum, or isothermal decomposition at low temperatures, was found to induce pure decomposition of LiBH₄, whilst mixed decomposition of LiBH₄ + Mg and formation of MgB₂ were achieved via high-temperature isothermal dehydrogenation.