Microscale Photopatterning of Through-thickness Modulus in a Monolithic and Functionally Graded 3D Printed Part

3D printing is transforming traditional processing methods for applications ranging from tissue engineering to optics. To fulfill its maximum potential, 3D printing requires a robust technique for producing structures with precise three-dimensional (x, y and z) control of mechanical properties. Previous efforts to realize such spatial control of modulus within 3D printed parts have largely focused on low-resolution (mm to cm scale) multi-material processes and grayscale approaches that spatially vary the modulus in the x-y plane and energy dose-based (E = I ₀ t _exp) models that do not account for the resin's sub-linear response to irradiation intensity. Here, we demonstrate a novel approach for through-thickness (z) voxelated control of mechanical properties within a single-material, monolithic part. Control over the local modulus is enabled by a predictive model that incorporates the observed non-reciprocal dose response of the material. The model is validated by an application of atomic force microscopy to map the through-thickness modulus on multi-layered 3D parts. Overall, both smooth gradations (30 MPa change over ≈75 microm) and sharp step-changes (30 MPa change over ≈5 microm) in modulus are realized in poly(ethylene glycol) diacrylate based 3D constructs, paving the way for advancements in tissue engineering, stimuli-responsive 4D printing and graded metamaterials.