Endogenous nitric oxide-generating surfaces via polydopamine-copper coatings for preventing biofilm dispersal and
Jayanti Mendhi1, Srinivas Sulugodu Ramachandra2, Indira Prasadam1
1Institute of Health and Biomedical Innovation, Queensland University of Technology, Brisbane, Australia.
Introduction:
Peri-implantitis is a bacterially induced inflammatory disease which affects the hard and soft tissues around a dental implant. Microbial biofilm formation is an important causative factor in peri-implantitis. The aim of this study is to develop an effective multifunctional surface coating for antimicrobial property and to counteract oral biofilm-associated infections via a single polydopamine copper coating (PDAM@Cu) on titanium implant surface to regulate endogenous nitric oxide (NO) generation.
Methods:
PDAM@Cu coatings were made with different concentrations of CuCl2 on titanium surfaces with a simple dip coating technique. Coatings were characterised to evaluate Cu concentrations as well as NO release rates from the coatings. Further, salivary biofilms were made on the coatings using Brain Heart Infusion (BHI) media in an anaerobic chamber. Biofilms were prepared with three different mixtures, one of which was saliva only, the second had an addition of sheep's blood, and the third was prepared with NO donors S-nitrosoglutathione (GSNO) and L-glutathione (GSH) in the mixture of saliva and blood to evaluate the effects of endogenously produced NO on biofilms. The effectiveness of coated surfaces on biofilms were assessed using four different methods, namely, crystal violet assay, scanning electron microscopy imaging, 2,3-bis (2-methoxy-4-nitro-5-sulfophenyl)-5-[(phenylamino) carbonyl]-2H-tetrazolium hydroxide (XTT) metabolic assay, and live/dead staining.
Results:
NO release rates could be controlled with different Cu concentration in PDAM@Cu coatings. NO generated from the PDAM@Cu coatings effectively induced dispersal of biofilms shown by the reduction in biofilm biomass as well as reduced biofilm attachment in samples prepared with blood and NO donors. Cu ions released from the PDAM@Cu coatings resulted in killing of the dispersed bacteria, which was evidenced by the live/dead cell staining and reduced metabolic activity noted from the XTT assay. In contrast, samples prepared with saliva showed no significant reduction in biofilms, indicating the important effect of endogenously generated NO on biofilm dispersal.
Conclusion:
In conclusion, PDAM@Cu coatings with NO generating surfaces have a dual anti-biofilm function, with a synergistic effect on biofilm dispersal from regulated NO generation and bactericidal effects from Cu ions from the coatings.