Encapsulation Strategies for Highly Stable Perovskite Solar Cells under Severe Stress Testing: Damp Heat, Freezing,...

A key direction toward managing extrinsic instabilities in perovskite solar cells (PSCs) is encapsulation. Thus, a suitable sealing layer is required for an efficient device encapsulation, preventing moisture and oxygen ingression into the perovskite layer. In this work, a solution-based, low-cost, and commercially available bilayer structure of poly(methyl methacrylate)/styrene-butadiene (PMMA/SB) is investigated for PSCs encapsulation. Encapsulated devices retained 80% of the initial power conversion efficiency (PCE) at 85 °C temperature and 85% relative humidity after 100 h, while reference devices without SB (only PMMA) suffer from rapid and intense degradation after only 2 h, under the same condition. In addition, encapsulated devices retained 95% of the initial PCE under -15 °C freezing temperature after 6 h and retained ∼80% of the initial PCE after immersion in HCl (37%) for 90 min. Moreover, applying an additional aluminum metal sheet on the PMMA/SB protective bilayer leads to the improvement of device stability up to 500 h under outdoor illumination, retaining almost 90% of the initial PCE. Considering the urge to develop reliable, scalable, and simple encapsulation for future large-area PSCs, this work establishes solution-based bilayer encapsulation, which is applicable for flexible solar modules as well as other optoelectronic devices such as light-emitting devices and photodetectors.improvement of device stability up to 500 h under outdoor illumination, retaining almost 90% of the initial PCE. Considering the urge to develop reliable, scalable, and simple encapsulation for future large-area PSCs, this work establishes solution-based bilayer encapsulation, which is applicable for flexible solar modules as well as other optoelectronic devices such as light-emitting devices and photodetectors.