Fatigue Life Prediction of Machined Specimens with the Consideration of Surface Roughness

Xiaochun Zhu1, Zhurong Dong1, Yachen Zhang1

  • 1School of Automotive and Transportation Engineering, Shenzhen Polytechnic, Shenzhen 518055, China.

Materials (Basel, Switzerland)
|September 28, 2021
PubMed

Keywords:
bending fatigue testfatigue life predictionfatigue notch factorsurface roughness

More Related Videos

Knowledge Based Cloud FE Simulation of Sheet Metal Forming Processes11:05

Knowledge Based Cloud FE Simulation of Sheet Metal Forming Processes

Published on: December 13, 2016

12.4K
Ultrasonic Fatigue Testing in the Tension-Compression Mode06:54

Ultrasonic Fatigue Testing in the Tension-Compression Mode

Published on: March 7, 2018

10.9K

Related Concept Videos

Fatigue01:21

Fatigue

Fatigue occurs when materials rupture under repeated or fluctuating loads, even at stress levels far below their static breaking strength. It typically results in brittle failure, even for ductile materials. It is a critical consideration in designing machines and structural components subjected to repetitive or varying loads. The nature of these loadings can range from fluctuating loads like unbalanced pump impellers causing vibrations to repeatedly bending a thin steel rod wire back and forth...
289
Fatigue Strength of Concrete01:22

Fatigue Strength of Concrete

Fatigue, in the context of materials science and engineering, refers to the weakening or failure of a material caused by repeatedly applied loads, even if these loads are below the strength limit of the material. Fatigue strength in concrete is a critical property that influences its durability and longevity. Concrete can fail in two ways due to fatigue. Static fatigue or creep rupture occurs under a constant load or one that increases slowly. The other failure mode is due to cyclical or...
328
Major Losses in Pipes01:28

Major Losses in Pipes

When a fluid flows through a pipe, it experiences energy losses due to frictional resistance along the pipe walls, known as major losses. These energy losses result in a pressure drop, which varies based on the flow conditions — whether laminar or turbulent — and the specific physical properties of the fluid and pipe.
Fluid flow can be classified as laminar or turbulent, primarily based on the Reynolds number. This dimensionless number reflects the relative influence of inertial to...
1.4K
Yield Criteria for Ductile Materials under Plane Stress01:25

Yield Criteria for Ductile Materials under Plane Stress

In designing structural elements and machine parts using ductile materials, it is crucial to ensure that these components withstand applied stresses without yielding. Yielding is initially determined through a tensile test, which evaluates the material's response to uniaxial stress. However, tensile stress is insufficient when components face biaxial or plane stress conditions This condition requires advanced criteria to predict failure.
The Maximum Shearing Stress Criterion, also known as...
250
Design Example: Deciding Thickness of Lubricating Fluid in a Shaft01:23

Design Example: Deciding Thickness of Lubricating Fluid in a Shaft

Effective lubrication between a rotating shaft and its bearing housing is essential in rotating machinery to minimize friction, wear, and energy loss. With carefully controlled thickness and viscosity, the lubricant layer prevents metal-to-metal contact, ensuring smooth operation.
To calculate the required thickness of the lubricant layer, the tangential velocity at the shaft's surface must first be determined. This velocity is calculated by converting the rotational speed to angular...
181
Design Consideration01:22

Design Consideration

Designing a structure involves a series of considerations, primarily the material's ultimate strength, calculated through tests that measure changes under increased force until the material reaches its breaking point or limit. The ultimate load, where the material breaks, is divided by its original cross-sectional area, resulting in the ultimate normal stress or strength. The ultimate shearing stress is another significant factor taken into account.
The factor of safety is another key...
374