Modulation of Ferroelectric and Optical Properties of La/Co-Doped KNbO3 Ceramics
Xue Zhang1, Ruijuan Qi1, Shangwei Dong1
1Key Laboratory of Polar Materials and Devices (MOE), Department of Electronic Sciences, East China Normal University, Shanghai 200241, China.
Abstract:
The phase transition, microscopic morphology and optical and ferroelectric properties are studied in a series of La- and Co-doped KNbO3-based ceramics. The results show that the doping induces the transformation from the orthorhombic to the cubic phase of KNbO3, significantly reduces the optical bandgap and simultaneously evidently improves the leakage, with a slight weakening of ferroelectric polarization. Further analysis reveals that (i) the Co doping is responsible for the obvious reduction of the bandgap, whereas it is reversed for the La doping; (ii) the slight deterioration of ferroelectricity is due to the doping-induced remarkable extrinsic defect levels and intrinsic oxygen vacancies; and (iii) the La doping can optimize the defect levels and inhibit the leakage. This investigation should both provide novel insight for exploring the bandgap engineering and ferroelectric properties of KNbO3, and suggest its potential applications, e.g., photovoltaic and multifunctional materials.
Related Concept Videos
01:31Ferromagnetism
03:02Colors and Magnetism
When atoms or molecules absorb light at the proper frequency, their electrons are excited to higher-energy orbitals. For many main group atoms and molecules, the absorbed photons are in the ultraviolet range of the electromagnetic spectrum, which cannot be detected by the human eye. For coordination compounds, the energy difference between the d orbitals often allows photons in the visible range to be absorbed and emitted, which is seen as colors by the human...