Embedding constructed refractive index graded antireflective coating with high abrasion resistance and environmental...

Polycarbonate (PC) is a durable and transparent optical plastic material commonly used as shatter-resistant alternative to traditional optical glass. Broadband antireflective (AR) coatings with excellent mechanical strength and environmental stability are essential for PC to achieve high light transmission and visual quality. In this work, chloroform vapor treatment was employed to partially embed the silica coating into the PC substrate for adhesion enhancement, which also divided the silica coating layer into bottom and middle layers with different refractive indices. The contact between the silica nanoparticles and the substrate was transformed from "point-contact" to "area-contact", which enhanced the adhesion between coating and PC substrate. After the deposition of a top layer coating consisted of silica nanoparticles with smaller diameter, a triple-layer refractive index graded AR structure was constructed. Hexamethyldisilazane vapor surface modification was performed to decrease the surface free energy of top coating layer. The triple-layer coating coated PC exhibits superior antireflection property with an average reflectance of only 0.43% over a wide wavelength range of 400-1000 nm. After 100 times of friction or 5 months of exposure to a contaminated environment, the reflectance of coated PC shows barely noticeable difference, indicating its excellent mechanical strength and environmental stability.