Exploring the Dual Characteristics of CH₃OH Adsorption to Metal Atomic Structures on Si (111)-7 × 7 Surface

Metal atoms were deposited on an Si (111)-7 × 7 surface, and they were adsorbed with alcohol gases (CH₃OH/C₂H₅OH/C₃H₇OH). Initially, C_nH_2n+1OH adsorption was simply used as an intermediate layer to prevent the chemical reaction between metal and Si atoms. Through scanning tunneling microscopy (STM) and a mass spectrometer, the C_nH_2n+1OH dissociation process is further derived as the construction of a surface quasi-potential with horizontal and vertical directions. With the help of three typical metal depositions, the surface characteristics of CH₃OH adsorption are more clearly presented in this paper. Adjusting the preheating temperature, the difference of thermal stability between CH₃O^- and H⁺ could be obviously derived in Au deposition. After a large amount of H⁺ was separated, the isolation characteristic of CH₃O^- was discussed in the case of Fe deposition. In the process of building a new metal-CH₃O^--H⁺ model, the dual characteristics of CH₃OH were synthetically verified in Sn deposition. CH₃O^- adsorption is prone to influencing the interaction between the metal deposition and substrate surface in the vertical direction, while H⁺ adsorption determines the horizontal behavior of metal atoms. These investigations lead one to believe that, to a certain extent, the formation of regular metal atomic structures on the Si (111)-7 × 7-CH₃OH surface is promoted, especially according to the dual characteristics and adsorption models we explored.