The Effect of Toothpastes Containing Natural Ingredients Such As Theobromine and Caffeine on Enamel Microhardness: An...

The current study aimed to investigate the effect of biocompatible kinds of toothpastes containing natural ingredients such as theobromine and caffeine on the enamel microhardness after demineralization. 72 maxillary premolar teeth extracted for orthodontic purposes were used in this study. Primary enamel surface microhardness examinations were performed using a Digital Micro Vickers Hardness Tester following the Knoop technique (50 g load for 15 s with three indentations at various points). The specimens were immersed in lactic acid (pH = 5.4) for 7 days, washed with distilled water, dried, and then retested for microhardness. According to the type of toothpaste used for brushing, all specimens were categorized as follows: Group 1, Theodent classic® toothpaste (theobromine); Group 2, Power Energy toothpaste (caffeine); Group 3, Colgate toothpaste (fluoride); and Group 4, distilled water as the negative control. The specimens were retested for enamel microhardness after brushing 2 times a day for one month. After brushing with different types of toothpaste, for all experiment groups, the increase in microhardness values in the demineralized enamel surfaces was significant and there were significant differences between them (p value <0.05). The fluoride group had the highest microhardness and had a significant difference with the caffeine and distilled water groups, but there was no significant difference with the theobromine group (p value <0.05). In the theobromine group, the hardness was considerably higher than in the caffeine and distilled water groups. There was no significant difference between the caffeine and distilled water groups. Theobromine toothpaste had the same remineralization effect as that of fluoride toothpaste, while caffeine toothpaste had no positive effect on the remineralization process.