Post-cure heat treatments influence on mechanical and optical properties of resin composites

This study evaluated the effect of post-cure heat treatment (PCHT) on the Knoop microhardness (KHN), degree of conversion (DC), color changes, and contrast ratio (CR) of four resin composites (RCs): Z100 (3M ESPE), Z350 XT (3M ESPE), Estelite Omega (Tokuyama) and Empress Direct (Ivoclar Vivadent). Specimens (12 × 1 mm) were prepared for each material (n = 10 / group). After curing, samples were subjected to PCHT for 10 min at 100°C or 170°C. Control group was maintained at room temperature (24°C) for the same time. The DC was analyzed by FT-NIR immediately and 24 h after the PCHT (n = 3 / group). KHN was analyzed 24 h after PCHT (n = 10 / group). According to CIEDE2000 (∆E00), color measurements were obtained immediately after curing, five minutes after PCHT, and after seven days of storage in water, coffee, and red wine. Data were analyzed by One and Two-Way ANOVA (p < 0.05). Z100, Z350, and Estelite Omega showed increases in KHN with increased temperature (p < 0.05). PCHT at 100°C and 170°C led to a higher DC of all RCs (p < 0.05). Initially, the PCHT lead to increased ∆E00 values (p < 0.05), which was decreased after immersion in coffee and wine (p < 0.05). Considering the effect of PCHT and staining solutions, lower color changes were observed in the thermally treated specimens (p < 0.05). Taken collectively, the results suggest the PCHT as an economical and practical alternative to enhance direct RC's properties in direct-indirect and indirect restorations.