Progresses in synthetic technology development for the production of L-lactide

Xiangkun Meng1, Lei Yu1, Yitao Cao2

  • 1School of Chemistry and Chemical Engineering, Yangzhou University, Yangzhou, Jiangsu 225002, China. yulei@yzu.edu.cn.

Organic & Biomolecular Chemistry
|November 17, 2021
PubMed

More Related Videos

Fabricating Superhydrophobic Polymeric Materials for Biomedical Applications09:22

Fabricating Superhydrophobic Polymeric Materials for Biomedical Applications

Published on: August 28, 2015

19.3K
Designed for Molecular Recycling: A Lignin-Derived Semi-aromatic Biobased Polymer10:22

Designed for Molecular Recycling: A Lignin-Derived Semi-aromatic Biobased Polymer

Published on: November 30, 2020

3.6K

Related Concept Videos

Step-Growth Polymerization: Overview01:03

Step-Growth Polymerization: Overview

Step-growth or condensation polymerization is a stepwise reaction of bi or multifunctional monomers to form long-chain polymers. As all the monomers are reactive, most of the monomers are consumed at the early stages of the reaction to form small chains of reactive oligomers, which then combine to form long polymer chains in the late stages. Hence, the reaction has to proceed for a long time to achieve high molecular weight polymers.
Many natural and synthetic polymers are produced by...
3.8K
Ziegler–Natta Chain-Growth Polymerization: Overview01:17

Ziegler–Natta Chain-Growth Polymerization: Overview

Ziegler–Natta polymerization is another form of addition or chain‐growth polymerization used for synthesizing linear polymers over branched polymers. The catalyst used for polymerization is the Ziegler–Natta catalyst, named after Karl Ziegler and Giulio Natta, who developed it in 1953. This catalyst is an organometallic complex of titanium tetrachloride and triethyl aluminum, with the active form of the catalyst being an alkyl titanium compound. Using the Ziegler–Natta...
3.5K
Types of Step-Growth Polymers: Polyesters01:20

Types of Step-Growth Polymers: Polyesters

The introduction of polyesters has brought major development to the textile industry. The wrinkle-free behavior of polyester blends has eliminated the need for starching and ironing clothes.
Polyesters are commonly prepared from terephthalic acid and ethylene glycol; the crude product is known as poly(ethylene terephthalate) or PET. However, polyesters are synthesized industrially by transesterification of dimethyl terephthalate with ethylene glycol at 150 °C. The two reactants and the...
2.4K
Olefin Metathesis Polymerization: Overview01:13

Olefin Metathesis Polymerization: Overview

Recently, the development of olefin metathesis polymerization advanced the field of polymer synthesis. Simply put, the reorganization of substituents on their double bonds between two olefins in the presence of a catalyst is known as the olefin metathesis reaction. The use of metathesis reaction for polymer synthesis is called olefin metathesis polymerization.
Ruthenium-based Grubbs catalyst is the most commonly used catalyst for olefin metathesis polymerization. Grubbs catalyst consists...
2.3K
Anionic Chain-Growth Polymerization: Overview01:20

Anionic Chain-Growth Polymerization: Overview

The polymerization process that involves carbanion as an intermediate is called anionic polymerization. It is also a type of addition or chain-growth polymerization. Anionic polymerization gets initiated by a strong nucleophile such as an organolithium or a Grignard reagent. The most commonly used initiator for anionic polymerization is butyl lithium. Monomers involved in anionic polymerization must possess a vinyl group bonded to one or two electron-withdrawing groups. For instance,...
2.2K