Realizing Superior Redox Kinetics of Hollow Bimetallic Sulfide Nanoarchitectures by Defect-Induced Manipulation...

As a typical battery-type material, CuCo₂ S₄ is a promising candidate for supercapacitors due to the high theoretical specific capacity. However, its practical application is plagued by inherently sluggish ion diffusion kinetics and inferior electrical transport properties. Herein, sulfur vacancies are incorporated in CuCo₂ S₄ hollow nanoarchitectures (HNs) to accelerate redox reactivity. Experimental analyses and theoretical investigations uncover that the generated sulfur vacancies increase the active electron states, reduce the adsorption barriers of electrolyte ions, and enrich reactive redox species, thus achieving enhanced electrochemical performance. Consequently, the deficient CuCo₂ S₄ with optimized vacancy concentration presents a high specific capacity of 231 mAh g^-1 at 1 A g^-1 , a ≈1.78 times increase compared to that of pristine CuCo₂ S₄ , and exhibits a superior rate capability (73.8% capacity retention at 20 A g^-1 ). Furthermore, flexible solid-state asymmetric supercapacitor devices assembled with the deficient CuCo₂ S₄ HNs and VN nanosheets deliver a high energy density of 61.4 W h kg^-1 at 750 W kg^-1 . Under different bending states, the devices display exceptional mechanical flexibility with no obvious change in CV curves at 50 mV s^-1 . These findings provide insights for regulating electrode reactivity of battery-type materials through intentional nanoarchitectonics and vacancy engineering.