Sol-Gel Synthesis and Characterization of YSZ Nanofillers for Dental Cements at Different Temperatures
Anastasia Beketova1, Anna Theocharidou1, Ioannis Tsamesidis1
1Department of Prosthodontics, School of Dentistry, Faculty of Health Sciences, Aristotle University of Thessaloniki, 54124 Thessaloniki, Greece.
Background:
Yttria-stabilized zirconia nanoparticles can be applied as fillers to improve the mechanical and antibacterial properties of luting cement. The aim of this study was to synthesize yttria-stabilized zirconia nanoparticles by the sol-gel method and to investigate their composition, structure, morphology and biological properties.
Methods:
Nanopowders of ZrO2 7 wt% Y2O3 (nY-ZrO) were synthesized by the sol-gel method and were sintered at three different temperatures: 800, 1000 and 1200 °C, and their composition, size and morphology were investigated. The biocompatibility was investigated with human gingival fibroblasts (hGFs), while reactive oxygen species (ROS) production was evaluated through fluorescence analysis.
Results:
All synthesized materials were composed of tetragonal zirconia, while nanopowders sintered at 800 °C and 1000 °C additionally contained 5 and 20 wt% of the cubic phase. By increasing the calcination temperature, the crystalline size of the nanoparticles increased from 12.1 nm for nY-ZrO800 to 47.2 nm for nY-ZrO1200. Nano-sized particles with good dispersion and low agglomeration were received. Cell culture studies with human gingival fibroblasts verified the nanopowders' biocompatibility and their ROS scavenging activity.
Conclusions:
the obtained sol-gel derived nanopowders showed suitable properties to be potentially used as nanofillers for dental luting cement.