Nonlinear Absorption and Refraction of Highly Monodisperse and Luminescent ZnTe Quantum Dots and Their Self-Assembled...

Zinc telluride (ZnTe) quantum dots (QDs) were synthesized by a unique supersaturation-controlled aqueous route. For a given pH, increasing the degree of initial supersaturation led to a decrease in the average diameter (d _avg) of the QDs and increased monodispersity. Three samples of ZnTe QDs having average sizes of 0.8, 1.7, and 2.2 nm were synthesized (hence named ZnTe_0.8, ZnTe_1.7, and ZnTe_2.2). Nonlinear absorption (NLA) and nonlinear refraction (NLR) of these colloidal ZnTe QDs of different sizes were investigated by the Z-scan technique using a continuous He-Ne laser (632.8 nm, 15 mW). Isotropic assembly of ZnTe_2.2 leads to the formation of nanoballs (hence named ZnTe_NB). The NLA profile of smaller QDs, ZnTe_1.7 and ZnTe_0.8, was found to follow a three-photon absorption (3PA) model, while relatively bigger QDs, ZnTe_2.2, followed a two-photon absorption (2PA) model. On moving from ZnTe_0.8 to ZnTe_1.7, the three-photon absorption coefficient (γ) decreases by 26% (3.00 × 10^-4 → 2.21 × 10^-4 cm³/MW²). The two-photon absorption coefficient (β) for ZnTe_2.2 is 0.3 cm/MW. For a 63% decrease in average diameter (2.2 → 0.8 nm), the refractive index (n ₂) increases by 45% (2.48 × 10^-2 → 3.6 × 10^-2 cm²/MW). Overall, the NLR coefficient shows a decreasing trend with size. Upon isotropic self-assembly, ZnTe_NB, there is a significant increase in the NLR coefficient by 40% (2.48 × 10^-2 → 3.48 × 10^-2 cm²/MW) and a simultaneous decrease in the NLA coefficient by 45% (0.3 → 0.166 cm/MW). The figure of merit was also determined for all of the samples, and it was found that ZnTe_2.2 and ZnTe_0.8 were best suited for all-optical device applications. Further, the self-assembled nanostructures are promising for making optical waveguides for supercontinuum generation (SCG).