Surface and bulk properties of zirconia as a function of composition and aging

Yttria-stabilized zirconia (Y-SZ) materials with different levels of translucency have been used for indirect dental restorations. Y-SZ composition and microstructure are modified to improve translucency, and it is not clear how these materials respond to aging. This study evaluated the effect of hydrothermal aging (HA) performed in an autoclave on the properties of four dental Y-SZ materials with different compositions. Sintered bar-shaped specimens (14 x 4 x 2 mm) were prepared from four different zirconia-based materials (n = 40): low translucency 3 mol % Y-SZ (3Y-LT; Ceramill ZI, Amann Girrbach); high translucency 4 mol % Y-SZ (4Y-HT; Ceramill Zolid); and two high translucency 5 mol % Y-SZ (5Y-HT - Lava Esthetic, 3M; 5Y-SHT - Ceramill Zolid FX). Fully sintered specimens were exposed to HA for different times (control - 0 h, 5 h, 10 h, or 15 h at 134 °C, 2 bar pressure) and characterized for surface roughness, flexural strength (three-point bending), hardness and elastic modulus (nanoindentation), surface wettability (sessile drop technique) and crystalline content (x-ray diffraction, XRD). Data was analyzed by two-way ANOVA and Tukey HSD (p < 0.05). Zirconia composition significantly affected roughness (p = 0.016). Zirconia*aging interaction affected flexural strength (p = 0.012), surface wettability (p < 0.001), and hardness (p = 0.002). Zirconia composition (p = 0.011) and aging (p = 0.001) affected elastic modulus, while the interaction effect was not significant (p = 0.94). HA affects zirconia-based materials in different degrees. For 3Y-LT and 4Y-HT, surface and bulk properties were affected by aging to a similar extent. However, surface and bulk properties may change during clinical use as a result of prolonged degradation of Y-SZ.